The typical strategy used to control the degradation of a th

The typical strategy used to control the degradation of a thermoplastic during use is to: use prepay mers to initiate oxidation mix it with thermosets increase the molecular weight lower the melting temperature increase the amount of monomers use a variety of protective additives During crevice corrosion, oxygen-rich areas act as the anode while oxygen depleted areas act as the cathode. True False The size of an internal crack that can tolerated at a stress of 100 MPa for a material with K_Ic of 100 MPa.m^1/2 is: 65 mm 100 mm 195 mm 254 mm 508 mm 603 mm 694 mm 742 mm 815 mm 888 mm 934 mm 1682 cm Uranium with a PBR of 3.05 is likely to develop a protective oxide on the surface. True False

Solution

7.use a variety of protective additives

8.true

9.100mm

10.true